熱遮へいコーティング膜の力学挙動のX線的研究
http://hdl.handle.net/10191/17654
http://hdl.handle.net/10191/17654dd9de1c8-5289-46cf-a630-3a8e06bbae49
名前 / ファイル | ライセンス | アクション |
---|---|---|
ZQ_49(1)_117-122.pdf (1.6 MB)
|
|
Item type | 学術雑誌論文 / Journal Article(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2012-04-05 | |||||
タイトル | ||||||
タイトル | 熱遮へいコーティング膜の力学挙動のX線的研究 | |||||
タイトル | ||||||
タイトル | 熱遮へいコーティング膜の力学挙動のX線的研究 | |||||
言語 | en | |||||
言語 | ||||||
言語 | jpn | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | X-ray stress measurement | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Thermal barrier coating | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Plasma splay coating | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Residual stress | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | Ceramics | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
資源タイプ | journal article | |||||
その他のタイトル | ||||||
その他のタイトル | X-Ray Study on Mechanical Behavior of Thermal Barrier Coated Film | |||||
著者 |
鈴木, 賢治
× 鈴木, 賢治× 町屋, 修太郎× 田中, 啓介× 坂井田, 善久 |
|||||
著者別名 | ||||||
識別子Scheme | WEKO | |||||
識別子 | 39880 | |||||
姓名 | Suzuki, Kenji | |||||
著者別名 | ||||||
識別子Scheme | WEKO | |||||
識別子 | 39881 | |||||
姓名 | Machiya, Shutaro | |||||
著者別名 | ||||||
識別子Scheme | WEKO | |||||
識別子 | 39882 | |||||
姓名 | Tanaka, Keisuke | |||||
著者別名 | ||||||
識別子Scheme | WEKO | |||||
識別子 | 39883 | |||||
姓名 | Sakaida, Yoshihisa | |||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | Thermal barrier coating (TBC)of 8 wt% Y_2O_3-ZrO_2 was made by low-pressure plasma spraying. The coated film with 0.3 mm in thickness was removed from the substrate of Nimonic-263 by electropolishing. Tension and compression tests of removed films were conducted by using a specially designed gap jig.TBC films showed stress relaxation while keeping the displacement constant both tensile and compressive deformation. The X-ray method was used to measure the stress in the TBC film under bending. The stress measured by the X-ray method changed proportionally to the bending stress up to the magnitude of about 10 MPa both in tension and compression. When the bending stress of about 20 MPa was applied to the films, the X-ray stress did not increase because of sliding of the lamella structure. The sliding stress between lamellae was determined from the residual curvature of films after bending. It was about 10 MPa, which agreed with limit stress measured by the X-ray method. | |||||
書誌情報 |
材料 en : 材料 巻 49, 号 1, p. 117-122, 発行日 2000-01 |
|||||
出版者 | ||||||
出版者 | 日本材料学会 | |||||
ISSN | ||||||
収録物識別子タイプ | ISSN | |||||
収録物識別子 | 05145163 | |||||
書誌レコードID | ||||||
収録物識別子タイプ | NCID | |||||
収録物識別子 | AN00096175 | |||||
著者版フラグ | ||||||
値 | publisher |