ログイン
言語:

WEKO3

  • トップ
  • ランキング
To
lat lon distance
To

Field does not validate



インデックスリンク

インデックスツリー

メールアドレスを入力してください。

WEKO

One fine body…

WEKO

One fine body…

アイテム

{"_buckets": {"deposit": "386bc0cd-8adb-4a1e-80f9-ffab7ecc2589"}, "_deposit": {"id": "25693", "owners": [], "pid": {"revision_id": 0, "type": "depid", "value": "25693"}, "status": "published"}, "_oai": {"id": "oai:niigata-u.repo.nii.ac.jp:00025693", "sets": ["456", "1313"]}, "item_7_alternative_title_1": {"attribute_name": "その他のタイトル", "attribute_value_mlt": [{"subitem_alternative_title": "Study on the incidence of marginal microleakage of various types of composite resin restorations and the clinical procedure to avoid microleakage"}]}, "item_7_biblio_info_6": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2002-12", "bibliographicIssueDateType": "Issued"}, "bibliographicIssueNumber": "2", "bibliographicPageEnd": "57", "bibliographicPageStart": "49", "bibliographicVolumeNumber": "32", "bibliographic_titles": [{"bibliographic_title": "新潟歯学会雑誌"}, {"bibliographic_title": "新潟歯学会雑誌", "bibliographic_titleLang": "en"}]}]}, "item_7_description_4": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "Composite resin restorations which have been widely used in the clinics have a problem to bring about hypersensitivity and secondary dental caries due to the microleakage of enamel and dentinal margin caused by polymerization contraction. The purpose of this study is to verify the occurrence of microleakages and to certify the clinical technique in order to avoid microleakage by using three different types of resin bonding systems which are known to have enough bonding strength to dentin. After pretreatment of three types of resin bonding systems, composite resin was filled in the cervical cavities which had been prepared on extracted human premolars. Then three polishing groups, namely, immediately polished group, resin impregnation group and one week water-immersed before polishing group were examined. The specimens were stained and the marginal-leakage was measured under measuring microscope. Further the Laser Scanning Microscope was used to observe the pretreated surface of dentin and enamel. The elemental distribution on adhered surface was analyzed by Electron probe micro-analyzer. Results showed that microleakage was significant on the enamel margin more than on dentinal margin. The present investigation showed that one week water-immersed before polishing group and resin impregnation group have strong marginal seal even after mechanical cyclic load test and thermal load test. Further, the degree of decalcification on pretreated surface is significantly different by the pretreatment agents, and the distribution of elements on adhered dentin surface is dissimilar by the bonding agents because of their permeability into dentin. The present study showed that the complete elimination of marginal leakage is not perfect yet even with the presence of the three bonding systems used in this study. As a conclusion on clinical aspect it is recommended to avoid immediate-polishing or using of the resin impregnation method in order to lessen marginal microleakage.", "subitem_description_type": "Abstract"}, {"subitem_description": "これまで広く用いられてきたボンディングシステムによるコンポジットレジン修復では、いまだレジン自身の重合収縮の問題は解決されておらず、エナメル質窩緑部及び象牙質窩縁部での辺縁漏洩が原因で、臨床上、知覚過敏や二次齲蝕をおこすという問題点がある。本研究は、近年の特に象牙質への接着強化を標榜する各種レジンボンディングシステムを用いたコンポジットレジン修復物の辺縁漏洩の発生状態を明らかにし、その防止のための臨床技法を確立するために行われた。ヒト抜去小臼歯に一窩洞でエナメル質、象牙質両窩縁を有する歯頚部窩洞を形成し、3種のレジンボンディングシステムを用いてコンポジットレジン充填を行った。その後、当日研磨群、レジンインプレグネーション法群そして一週間水中浸漬後研磨群の研磨方法の異なる3群に分け、辺縁漏洩試験を行った。さらに走査型共焦点レーザー顕微鏡を用いて、各種レジンボンディングシステム前処理後の表面性状を観察し、Ⅹ線マイクロアナライザーにより接着境界面の元素分析を行った。その結果、象牙質窩緑よりエナメル質窩縁の方が微少漏洩が多く見られた。また、一週間水中浸漬後研磨群およびレジンインプレグネーション法を用いた群では、繰り返し荷重、熱サイクルのどちらの負荷を加えた場合でも、エナメル質窩縁、象牙質窩縁の両者で、高い辺縁封鎖性が得られた。しかし前処理剤の違いにより接着境界面の脱灰の程度は大きく異なり、さらにボンディング剤の象牙質への浸透性の違いから、材料により接着界面の元素分布も大きく異なることが明らかになり、現時点ではまだ改良の余地があることが示唆された。以上から臨床的にはいまだ当日研磨を避ける、もしくはレジンインプレグネーション法を行うという術式を加え微少漏洩を最小限に抑える必要があることが示された。", "subitem_description_type": "Abstract"}]}, "item_7_full_name_3": {"attribute_name": "著者別名", "attribute_value_mlt": [{"nameIdentifiers": [{"nameIdentifier": "151481", "nameIdentifierScheme": "WEKO"}], "names": [{"name": "Kobayashi, Yuji"}]}, {"nameIdentifiers": [{"nameIdentifier": "151482", "nameIdentifierScheme": "WEKO"}], "names": [{"name": "Okamoto, Akira"}]}]}, "item_7_publisher_7": {"attribute_name": "出版者", "attribute_value_mlt": [{"subitem_publisher": "新潟歯学会"}]}, "item_7_select_19": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_select_item": "publisher"}]}, "item_7_source_id_11": {"attribute_name": "書誌レコードID", "attribute_value_mlt": [{"subitem_source_identifier": "AN0018300X", "subitem_source_identifier_type": "NCID"}]}, "item_7_source_id_9": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "03850153", "subitem_source_identifier_type": "ISSN"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "小林, 裕二"}], "nameIdentifiers": [{"nameIdentifier": "151479", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "岡本, 明"}], "nameIdentifiers": [{"nameIdentifier": "151480", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2019-08-19"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "NS_32(2)_49-57.pdf", "filesize": [{"value": "2.7 MB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_free", "mimetype": "application/pdf", "size": 2700000.0, "url": {"label": "NS_32(2)_49-57.pdf", "url": "https://niigata-u.repo.nii.ac.jp/record/25693/files/NS_32(2)_49-57.pdf"}, "version_id": "68daba89-70e6-485f-ae74-c31f095c5333"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "Composite resin", "subitem_subject_scheme": "Other"}, {"subitem_subject": "microleakage", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Laser Scanning Microscope", "subitem_subject_scheme": "Other"}, {"subitem_subject": "Electron probe micro-analyzer", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "departmental bulletin paper", "resourceuri": "http://purl.org/coar/resource_type/c_6501"}]}, "item_title": "各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究"}, {"subitem_title": "各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究", "subitem_title_language": "en"}]}, "item_type_id": "7", "owner": "1", "path": ["456", "1313"], "permalink_uri": "http://hdl.handle.net/10191/23249", "pubdate": {"attribute_name": "公開日", "attribute_value": "2013-08-27"}, "publish_date": "2013-08-27", "publish_status": "0", "recid": "25693", "relation": {}, "relation_version_is_last": true, "title": ["各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究"], "weko_shared_id": null}
  1. 260 大学院医歯学総合研究科(歯)
  2. 20 紀要
  3. 01 新潟歯学会雑誌
  4. 第32巻第2号
  1. 0 資料タイプ別
  2. 03 紀要論文

各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究

http://hdl.handle.net/10191/23249
http://hdl.handle.net/10191/23249
a2070782-4f9d-4a6a-aac1-1f13c6452cd0
名前 / ファイル ライセンス アクション
NS_32(2)_49-57.pdf NS_32(2)_49-57.pdf (2.7 MB)
Item type 紀要論文 / Departmental Bulletin Paper(1)
公開日 2013-08-27
タイトル
タイトル 各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究
タイトル
言語 en
タイトル 各種コンポジットレジン修復物の辺縁部微少漏洩の発生状態とその防止のための臨床技法の確立に関する研究
言語
言語 jpn
キーワード
主題Scheme Other
主題 Composite resin
キーワード
主題Scheme Other
主題 microleakage
キーワード
主題Scheme Other
主題 Laser Scanning Microscope
キーワード
主題Scheme Other
主題 Electron probe micro-analyzer
資源タイプ
資源 http://purl.org/coar/resource_type/c_6501
タイプ departmental bulletin paper
その他のタイトル
その他のタイトル Study on the incidence of marginal microleakage of various types of composite resin restorations and the clinical procedure to avoid microleakage
著者 小林, 裕二

× 小林, 裕二

WEKO 151479

小林, 裕二

Search repository
岡本, 明

× 岡本, 明

WEKO 151480

岡本, 明

Search repository
著者別名
識別子 151481
識別子Scheme WEKO
姓名 Kobayashi, Yuji
著者別名
識別子 151482
識別子Scheme WEKO
姓名 Okamoto, Akira
抄録
内容記述タイプ Abstract
内容記述 Composite resin restorations which have been widely used in the clinics have a problem to bring about hypersensitivity and secondary dental caries due to the microleakage of enamel and dentinal margin caused by polymerization contraction. The purpose of this study is to verify the occurrence of microleakages and to certify the clinical technique in order to avoid microleakage by using three different types of resin bonding systems which are known to have enough bonding strength to dentin. After pretreatment of three types of resin bonding systems, composite resin was filled in the cervical cavities which had been prepared on extracted human premolars. Then three polishing groups, namely, immediately polished group, resin impregnation group and one week water-immersed before polishing group were examined. The specimens were stained and the marginal-leakage was measured under measuring microscope. Further the Laser Scanning Microscope was used to observe the pretreated surface of dentin and enamel. The elemental distribution on adhered surface was analyzed by Electron probe micro-analyzer. Results showed that microleakage was significant on the enamel margin more than on dentinal margin. The present investigation showed that one week water-immersed before polishing group and resin impregnation group have strong marginal seal even after mechanical cyclic load test and thermal load test. Further, the degree of decalcification on pretreated surface is significantly different by the pretreatment agents, and the distribution of elements on adhered dentin surface is dissimilar by the bonding agents because of their permeability into dentin. The present study showed that the complete elimination of marginal leakage is not perfect yet even with the presence of the three bonding systems used in this study. As a conclusion on clinical aspect it is recommended to avoid immediate-polishing or using of the resin impregnation method in order to lessen marginal microleakage.
抄録
内容記述タイプ Abstract
内容記述 これまで広く用いられてきたボンディングシステムによるコンポジットレジン修復では、いまだレジン自身の重合収縮の問題は解決されておらず、エナメル質窩緑部及び象牙質窩縁部での辺縁漏洩が原因で、臨床上、知覚過敏や二次齲蝕をおこすという問題点がある。本研究は、近年の特に象牙質への接着強化を標榜する各種レジンボンディングシステムを用いたコンポジットレジン修復物の辺縁漏洩の発生状態を明らかにし、その防止のための臨床技法を確立するために行われた。ヒト抜去小臼歯に一窩洞でエナメル質、象牙質両窩縁を有する歯頚部窩洞を形成し、3種のレジンボンディングシステムを用いてコンポジットレジン充填を行った。その後、当日研磨群、レジンインプレグネーション法群そして一週間水中浸漬後研磨群の研磨方法の異なる3群に分け、辺縁漏洩試験を行った。さらに走査型共焦点レーザー顕微鏡を用いて、各種レジンボンディングシステム前処理後の表面性状を観察し、Ⅹ線マイクロアナライザーにより接着境界面の元素分析を行った。その結果、象牙質窩緑よりエナメル質窩縁の方が微少漏洩が多く見られた。また、一週間水中浸漬後研磨群およびレジンインプレグネーション法を用いた群では、繰り返し荷重、熱サイクルのどちらの負荷を加えた場合でも、エナメル質窩縁、象牙質窩縁の両者で、高い辺縁封鎖性が得られた。しかし前処理剤の違いにより接着境界面の脱灰の程度は大きく異なり、さらにボンディング剤の象牙質への浸透性の違いから、材料により接着界面の元素分布も大きく異なることが明らかになり、現時点ではまだ改良の余地があることが示唆された。以上から臨床的にはいまだ当日研磨を避ける、もしくはレジンインプレグネーション法を行うという術式を加え微少漏洩を最小限に抑える必要があることが示された。
書誌情報 新潟歯学会雑誌
en : 新潟歯学会雑誌

巻 32, 号 2, p. 49-57, 発行日 2002-12
出版者
出版者 新潟歯学会
ISSN
収録物識別子タイプ ISSN
収録物識別子 03850153
書誌レコードID
収録物識別子タイプ NCID
収録物識別子 AN0018300X
著者版フラグ
値 publisher
戻る
0
views
See details
Views

Versions

Ver.1 2021-03-01 12:03:20.947564
Show All versions

Share

Mendeley Twitter Facebook Print Addthis

Cite as

エクスポート

OAI-PMH
  • OAI-PMH JPCOAR
  • OAI-PMH DublinCore
  • OAI-PMH DDI
Other Formats
  • JSON
  • BIBTEX

Confirm


Powered by WEKO3


Powered by WEKO3