@article{oai:niigata-u.repo.nii.ac.jp:00001488,
 author = {Sato, Mineo and Ishigaki, Tadashi and Uematsu, Kazuyoshi and Toda, Kenji and Okawa, Hirokazu},
 issue = {9},
 journal = {Acta Crystallographica Section E, Acta Crystallographica Section E},
 month = {Aug},
 note = {Crystals of dilithium manganese(II) silicate were grown under high-temperature hydro­thermal conditions in the system LiOH—MnO2—SiO2. The title compound crystallizes in the βII-Li3PO4 structure type. The coordination polyhedra of all cations are slightly distorted tetra­hedra (m symmetry for MnO4 and SiO4), which are linked by corner-sharing to each other. The vertices of the tetra­hedra point to the same direction perpendicular to the distorted hexa­gonal close-packed (hcp) array of O atoms within which half of the tetra­hedral voids are occupied by cations. In comparison with the previous refinement from powder X-ray data [Dominko et al. (2006 [triangle]). Electrochem. Commun. 8, 217–222], the present reinvestigation from single-crystal X-ray data allows a more precise determination of the distribution of the Li+ and Mn2+ cations, giving a perfectly site-ordered structure model for both Li+ and Mn2+.},
 pages = {i68--i69},
 title = {Redetermination of the low-temperature polymorph of Li2MnSiO4 from single-crystal X-ray data},
 volume = {68},
 year = {2012}
}